VICTREX FG™ POLYMER 700 FPD

High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for composite manufacture, easy flow, FDA food contact compliant, colour natural.

Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications

Request a quote Download PDF

Material Properties
Physical	Nominal Value	Unit	Test Method
Density	1.30	g/cm³	ISO 1183
Apparent (Bulk) Density	0.30	g/cm³	ISO 1183
Average Particle Size - D50	10	µm	ISO 13320-1
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus¹ (23°C)	4100	MPa	ISO 527-1
Tensile Stress¹ (Break, 23°C)	100	MPa	ISO 527-2
Tensile Strain¹ (Break, 23°C)	15	%	ISO 527-2
Flexural Modulus¹ (23°C)	3900	MPa	ISO 178
Flexural Stress¹ (23°C)	170	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength¹ (23°C)	4.5	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength¹ (23°C)	No Break		ISO 180
Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature			ISO 11357-2
Onset	143	°C
Midpoint	147	°C
Melting Temperature	343	°C	ISO 11357-3
Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	130	Pa·s	ISO 11443

Typical Processing Information
Injection	Nominal Value	Unit
Drying Temperature	120 to 150	°C
Drying Time	3.0 to 5.0	hr
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	380 to 400	°C
Injection Notes
Important notes: 1) Processing conditions quoted in our datasheets are typical of those used in our processing laboratories Data for mould shrinkage should be used for material comparison. Actual mould shrinkage values are highly dependent on part geometry, mould configuration, and processing conditions. Mould shrinkage differs for along flow and across flow directions. “Along flow” direction is taken as the direction the molten material is travelling when it exits the gate and enters the mould. Mould shrinkage is expressed as a percent change in dimension of a specimen in relation to mould dimensions. 2) Data are generated in accordance with prevailing national, international and internal standards, and should be used for material comparison. Actual property values are highly dependent on part geometry, mould configuration and processing conditions. Properties may also differ for along flow and across flow directions. Detailed data available on our website www.victrex.com or upon request.

Notes

¹Results based on similar products